FEP 6100 聚全氟乙丙烯树脂

添加时间:2017-12-14  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
Teflon
 DuPontT Teflon® FEP 6100 Fluoropolymer Resin
Technical DataSheet
 
DuPontT Teflon® FEP 6100 fluoropolymer resin is a melt-processable fluoropolymer resin specifically designed for high-speed extrusion of thin coatings on small-gauge wires for twisted-pair constructions.As shown in Table 1, this resin provides the electrical and mechanical properties needed for low voltage applications. In addition, Teflon® FEP 6100 has a higher melt flow rate than most other fluoropolymer resins. This permits higher extrusion speeds and easier processing, making Teflon® FEP 6100 a cost-effective alternative for producing thin-wall extrusions.Teflon® FEP 6100 possesses a balance of processing and performance properties, which makes it an excellent choice for many applications. Like all Teflon® fluoropolymer resins, Teflon® FEP 6100 offers an excellent combination of properties:low flammabilityexceptional dielectric propertiesheat resistancetoughnessflexibilitylow coefficient of frictionnonstick characteristicsnegligible moisture absorptionchemical inertnessperformance at temperature extremesweather resistanceApplicationsTeflon® FEP 6100 is especially suitable for use in insulating data and telecommunications cables with excellent fire performance and physical properties as well as outstanding electrical performance. Cables insulated with Teflon® FEP 6100 have met the requirements of the NFPA 90A 'Standard for the Installation of Air-conditioning and Ventilating Systems'. To meet these requirements cables are tested using the NFPA 262 Standard Method of Test for Flame Travel and Smoke of Wires and Cables. This standard test method is used to qualify cables for installation in plenum spaces under the provisions of NFPA 90A. Teflon® FEP 6100 complies with ASTM 2116.Teflon® FEP 6100 is not recommended as a jacket material or as a heavy-walled insulation in constructions where significant thermal cycling may raisestress-cracking concerns.
 
DuPontT Teflon® FEP 6100 Fluoropolymer Resin Product details
产品类型:含氟聚合物>聚全氟乙丙烯FEP
产品状态:有售
代理销售:苏州希料能塑料 185 5121 3137 谭经理
 
DuPontT Teflon® FEP 6100 Fluoropolymer Resin Properties
物理性质 值和单位 测试条件 测试方法
比重 2.14 g/cc   ASTM D792
熔体流动 30 g/10 min   ASTM D2116
吸水率 < 0.01 %   24小时;ASTM D570
电气性能 值和单位 测试条件 测试方法
体积电阻率 >1.000E+018 ohm-cm   ASTM D 257
表面电阻率每平方 >1.000E+016 ohm   ASTM D 257
绝缘强度 53 kV/mm   100微米的薄膜;ASTM D149
电弧电阻 >300 sec   ASTM D495
介电常数 2.03 @Frequency 1000000 Hz ASTM D2520
耗散因子 0.00057 @Frequency 1000000 Hz ASTM D2520
加工性能 值和单位 测试条件 测试方法
加工温度 360-385℃   固化温度
热性能 值和单位 测试条件 测试方法
可燃性,UL94 V-0    
氧指数 >95 %   极限氧指数;ASTM D2863
熔点 264℃   ASTM D3418
机械性能 值和单位 测试条件 测试方法
摩擦系数 0.08-0.3   ASTM D1894
弯曲模量 0.52 Gpa   ASTM D790
悬臂梁缺口冲击强度 9999 J/m   ASTM D256
邵氏硬度 56   ASTM D2240
极限抗拉强度 20 Mpa   ASTM D1457
断裂伸长率 3   ASTM D1457
描述性的属性
耐气候性 20 在佛罗里达没有受到影响
硫酸传输, g/100sq in. 0.00001  
水传输, g/100sq in. 0.4  
红烟硝酸传输, g/100sq in. 7.5-1.4  
铝的耐盐性,小时 >744  
燃烧热 J/g 5100 ASTM D240
己烷传输, g/100sq in. 0.56  
哌啶传输, g/100sq in. 0.04  
喷砂钢板上的抗洗涤剂,小时 480  
乙酸乙酯的传输, g/100sq in. 0.76  
耐折度, # cycles, .18-.20 mm 5-80 E3  
耐化学溶剂性 Excellent  
铝的耐洗涤剂性,小时 744  
洗涤剂抵抗.喷砂铝,小时 600  
苯的传输, g/100sq in. 0.64  
四氯化碳传输, g/100sq in. 0.31  
醋酸传输, g/100sq in. 0.41  
丙酮传输, g/100sq in. 0.95  
苯乙酮的传输, g/100sq in. 0.5  
20%盐酸传输, g/100sq in. <0.02  
50%氢氧化钠传输, g/100sq in. <.02  