Plexiglas PMMA Resist zk5HF

Plexiglas® PMMA Resist zk5HF
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Resist zk5HF is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
 
Typical properties of impact-modified PLEXIGLAS® molding compounds are
﹒high weather resistance
﹒excellent transmission and clarity
﹒brilliant appearance
﹒the pleasant feel and sound of the moldings.
 
PLEXIGLAS® Resist zk5HF is characterized by the following special properties:
﹒high break resistance and impact strength
﹒improved resistance to stress cracking
﹒excellent flow.
 
Application:
Used for injection molding as well as for extruding sheets and profiles.
 
Examples:
applications involving thin walls and long flow paths; thin-walled components; items requiring accurate mold surface reproduction, such as very finely textured luminaire covers.
 
UL 黄卡2E65495-247821
含添加剂:冲击调节器
材料特点:高 ESCR(抗应力裂纹),高抗撞击,流动性佳,耐气候影响,高清晰度,外观良好
材料用途:保护性遮盖物,纺织应用,片材,墙板,铸模/模具/工具
产品形式:颗粒料
加工方法:挤出,注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Resist zk5HF
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.17 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 8.10 cm³/10min ISO 1133
吸水率     ISO 62
23℃,24 hr 1.9 %
平衡,23℃,50% RH 0.50 %
机械性能 额定值 单位制 测试方法
拉伸模量 2500 MPa ISO 527-2/1
拉伸应力(屈服) 55.0 MPa ISO 527-2/50
拉伸应变(屈服) 4.5 % ISO 527-2/50
断张率 25 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 50 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
维卡软化温度 96.0 ISO 306/B50
线形膨胀系数 - 流动(0 到 50℃) 0.000090 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率3 92.0 % ISO 13468-2
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <85.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 260
模具温度 50.0 到 70.0