Plexiglas PMMA Resist zk40

Plexiglas® PMMA Resist zk40
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Resist zk40 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
 
Typical properties of impact-modified PLEXIGLAS® molding compounds are
﹒excellent transmission and clarity
﹒brilliant appearance
﹒the pleasant feel and sound of the moldings.
 
PLEXIGLAS® Resist zk40 is characterized by the following special properties:
﹒very good break resistance and impact strength
﹒improved resistance to stress cracking
﹒AMECA listing.
 
Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.
 
Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware
 
含添加剂:冲击调节器
材料特点:高 ESCR(抗应力裂纹),高抗撞击,清晰度高,外观良好
材料用途:电器用具,柔软的把手,卫浴产品,文具,型材
产品形式:颗粒料
加工方法:共挤出成型,挤出,注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Resist zk40
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.13 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 0.700 cm³/10min ISO 1133
吸水率(平衡,23℃,50% RH) 0.38 % ISO 62
机械性能 额定值 单位制 测试方法
拉伸模量 1600 MPa ISO 527-2/1
拉伸应力(屈服) 42.0 MPa ISO 527-2/50
拉伸应变(屈服) 4.5 % ISO 527-2/50
断张率 30 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 80 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 92.0 ISO 75-2/B
1.8 MPa,未退火 85.0 ISO 75-2/A
玻璃转化温度 115 ISO 11357-2
维卡软化温度 94.0 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.00012 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率2 90.0 % ISO 13468-2
注射 额定值 单位制
干燥温度 <84.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 230 到 240
模具温度 50.0 到 70.0