Plexiglas PMMA Optical POQ66

Plexiglas® PMMA Optical POQ66
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
PLEXIGLAS® Optical POQ66 is an amorphous thermoplastic molding compound based on polymethylmethacrylate (PMMA).
 
In addition to the familiar properties of PLEXIGLAS® molding compounds, such as
﹒excellent light transmission and brilliance,
﹒very good weather resistance,
﹒high mechanical strength, surface hardness and mar resistance,
 
PLEXIGLAS® Optical POQ66 is distinguished by its
﹒guaranteed purity and clarity,
﹒high luminous efficiency in medium to long light paths,
﹒absolute colorlessness even in thick layers
﹒UL registration RTI90 by (fi) 746C.
 
Application:
PLEXIGLAS® Optical POQ66 is suitable for manufacturing extruded sheets to meet stringent optical requirements.
 
Examples:
Medium to large extruded light guide (Light Guide Panel) for display applications.
 
UL 黄卡2E65495-100986378
材料特点:High Hardness,Light Stabilized,高强度,流动性佳,耐气候影响,清晰度高
材料用途:Displays,Lighting Applications,光学应用
产品形式:颗粒料
加工方法:挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Optical POQ66
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 2.30 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 3200 MPa ISO 527-2/1
拉伸应力(断裂) 69.0 MPa ISO 527-2/5
拉伸应变(断裂) 4.0 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 20 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
玻璃转化温度 108 ISO 11357-2
维卡软化温度 104 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000080 cm/cm/℃ ISO 11359-2
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率3 92.0 % ISO 13468-2
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <94.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 240
模具温度 220 到 260