PMMA df23 8N 高强度,流动性佳,耐气候影响

添加时间:2013-11-27  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料

Plexiglas PMMA df23 8N

Plexiglas® PMMA df23 8N
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Satinice df23 8N, based on PLEXIGLAS® 8N, is characterized by diffuse scattering of light.
 
Typical properties of PLEXIGLAS® molding compound are
﹒good flow
﹒high mechanical strength, surface hardness and mar resistance
﹒very good weather resistance.
 
Special properties of PLEXIGLAS® Satinice df23 8N are
﹒excellent lightdiffusion combined with excellent light transmission.
 
Application:
Used for injection molding items for lighting engineering applications
 
Examples:
luminaire covers, projection screens and similar applications
 
Processing:
PLEXIGLAS® Satinice df23 8N can be processed on injection molding machines with 3-zone general purpose screws for engineering thermoplastics.
 
Physical Form / Packaging:
PLEXIGLAS® Satinice df molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags; other packaging on request.
 
材料特点:High Hardness,Light Stabilized,高强度,流动性佳,耐气候影响
材料用途:视频设备,照明漫射器
产品形式:颗粒料
加工方法:注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA df23 8N
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.19 g/cm³ ISO 1183
溶化体积流率(MVR)230℃/3.8 kg) 2.10 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 3300 MPa ISO 527-2/1
拉伸应力(断裂) 65.0 MPa ISO 527-2/5
拉伸应变(断裂) 2.5 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 1.8 kJ/m² ISO 179/1
简支梁缺口冲击强度(23℃) 16 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 103 ISO 75-2/B
1.8 MPa,未退火 98.0 ISO 75-2/A
玻璃转化温度 108 IEC 1006
维卡软化温度 109 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000063 cm/cm/℃ ISO 11359-2
可燃性 额定值 单位制 测试方法
热灯丝点火温度 700 IEC 60695-2-13
光学性能 额定值 单位制 测试方法
透射率2 81.0 % ISO 13468-2
补充信息 额定值 单位制 测试方法
Fire Rating B2   DIN 4102
Half-Value Angle 21.0 ° DIN 5036
挤出 额定值 单位制
干燥温度 <95.0
干燥时间 2.0 到 3.0 hr
熔体温度 220 到 260
模具温度 60.0 到 90.0