Plexiglas PMMA df22 zk6BR

Plexiglas® PMMA df22 zk6BR
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Satinice df22 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.
 
Typical properties of impact modified PLEXIGLAS® molding compound are
 
high break resistance and impact strength
﹒improved resistance to stress cracking
﹒good weather resistance
﹒high surface hardness and mar resistance
﹒the pleasant feel and sound of the moldings.
 
PLEXIGLAS® Satinice df22 zk6BR is characterized by the following special properties:
﹒very good lightdiffusion combined with excellent light transmission
﹒matte surfaces can be obtained by varying the extrusion parameters.
 
Application:
Used for extruding profiles and sheets, but also for injection molding items for lighting engineering applications
 
Examples:
applications that call for light diffusion combined with optimum transmission
 
Processing:
PLEXIGLAS® Satinice df22 zk6BR can be processed on extruders with 3-zone general purpose screws for engineering thermoplastics. The matte finish of profile surfaces depends very much on machine design (calibrating unit, polishing rolls) and cooling conditions. It can be enhanced by controlled temperature reduction.
 
Physical Form / Packaging:
PLEXIGLAS® Satinice df molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags; other packaging on request.
 
含添加剂:冲击调节器
材料特点:High Hardness,Light Stabilized,高 ESCR(抗应力裂纹),高强度,高抗撞击,耐气候影响
材料用途:片材,型材,照明漫射器
产品形式:颗粒料
加工方法:注射成型,挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA df22 zk6BR
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.15 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 1.40 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 1800 MPa ISO 527-2/1
拉伸应力(屈服) 45.0 MPa ISO 527-2/50
拉伸应变(屈服) 5.0 % ISO 527-2/50
断张率 40 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 6.5 kJ/m² ISO 179/1
简支梁缺口冲击强度(23℃) 54 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 99.0 ISO 75-2/B
1.8 MPa,未退火 93.0 ISO 75-2/A
玻璃转化温度 109 IEC 1006
维卡软化温度 98.0 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000090 cm/cm/℃ ISO 11359-2
可燃性 额定值 单位制 测试方法
热灯丝点火温度 700 IEC 60695-2-13
光学性能 额定值 单位制 测试方法
透射率2 86.0 % ISO 13468-2
补充信息 额定值 单位制 测试方法
Fire Rating B2   DIN 4102
Half-Value Angle 12.5 ° DIN 5036
挤出 额定值 单位制
干燥温度 <85.0
干燥时间 2.0 到 3.0 hr
熔体温度 230 到 260
模具温度 260