LNP STAT-LOY PMMA 9X05426C

添加时间:2013-02-22  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
LNP™ STAT-LOY™ Compound PMMA 9X05426C
 
Also known as:LNP™ Stat-loy™ Compound PDX-05426 CCS BL5-343-2 TP Product reorder name:9X05426C
LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yield 430 kgf/cm² ASTM D 638
Tensile Stress,break 410 kgf/cm² ASTM D 638
Tensile Strain,yield 6.7 % ASTM D 638
Tensile Strain,break 18.4 % ASTM D 638
Tensile Modulus,50mm/min 17800 kgf/cm² ASTM D 638
Flexural Stress 560 kgf/cm² ASTM D 790
Flexural Modulus 16900 kgf/cm² ASTM D 790
Tensile Stress,yield 42 MPa ISO 527
Tensile Stress,break 39 MPa ISO 527
Tensile Strain,yield 6.2 % ISO 527
Tensile Strain,break 20.3 % ISO 527
Tensile Modulus,1mm/min 1470 MPa ISO 527
Flexural Stress 44 MPa ISO 178
Flexural Modulus 1410 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 54 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 29 cm-kgf ASTM D 3763
Multiaxial Impact 7 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 79 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 67 ASTM D 648
CTE,-40℃ to 40℃,flow 1.01E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 1.08E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.01E-04 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 1.09E-04 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 79 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 70 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.14 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.82 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.98 % ISO 294
Density 1.13 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+09-1.E+11 Ohm-cm ASTM D 257
Surface Resistivity 1.E+09-1.E+11 Ohm ASTM D 257
Source GMD,last updated:2007/02/27
Parameter Injection Molding Value Unit
Drying Temperature 75-90
Drying Time 4 hrs
Maximum Moisture Content 0.01 %
Nozzle Temperature 215-240
Front-Zone 3 Temperature 215-240
Middle-Zone 2 Temperature 215-240
Rear-Zone 1 Temperature 215-240
Mold Temperature 25-90
Source GMD,last updated:2007/02/27