LNP THERMOCOMP PC DF0089

添加时间:2013-02-25  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料

LNP™ THERMOCOMP™ Compound PC DF0089

 

Also known as:LNP™ Thermocomp™ Compound DF-1008 FR LEX Product reorder name:DF0089
LNP THERMOCOMP* DF0089 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.

 

Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit Standard
Tensile Stress,break 1340 kgf/cm² ASTM D 638
Tensile Strain,break 1.7 % ASTM D 638
Tensile Modulus,50mm/min 139900 kgf/cm² ASTM D 638
Flexural Stress 1940 kgf/cm² ASTM D 790
Flexural Modulus 120200 kgf/cm² ASTM D 790
Tensile Stress,break 130 MPa ISO 527
Tensile Strain,break 1.6 % ISO 527
Tensile Modulus,1mm/min 12400 MPa ISO 527
Flexural Stress 203 MPa ISO 178
Flexural Modulus 12500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 54 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 82 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 46 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 10 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 137 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 138 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.589 g/cm³ ASTM D 792
Density 1.58 g/cm³ ISO 1183
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 1.6 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/09/28
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-325
Front-Zone 3 Temperature 320-330
Middle-Zone 2 Temperature 310-320
Rear-Zone 1 Temperature 295-305
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/28