PBT WV006 compound 含长玻璃纤维

添加时间:2014-03-19  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
LNP VERTON PBT WV006 compound
LNP™ VERTON™ PBT WV006 compound
聚丁烯对苯二甲酸酯
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
Also known as:LNP™ VERTON™ Compound WF-7006
Product reorder name:WV006
 
LNP VERTON* WV006 is a compound based on Polybutylene Terephalate resin containing Long Glass.
 
增强填料:含长玻璃纤维
定属记号:PBT
塑料牌号:PBT WV006
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/verton/wv006-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break 187 MPa ISO 527
Tensile Strain,break 2 % ISO 527
Tensile Modulus,1 mm/min 11570 MPa ISO 527
Flexural Stress 247 MPa ISO 178
Flexural Modulus 9780 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 56 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 30 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -40℃ 36 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 225 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.54 g/cm³ ISO 1183
Injection Molding Value Unit
Drying Temperature 120
Drying Time 4 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 250-260
Front-Zone 3 Temperature 250-260
Middle-Zone 2 Temperature 240-250
Rear-Zone 1 Temperature 230-245
Mold Temperature 65-120
Back Pressure 0.2-0.3 MPa
Screw Speed 30-70 rpm
PBT LNP™ VERTON™ COMPOUND
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.