PBT SHF4960 Resin 玻纤增强,阻燃V0,超高流动

添加时间:2014-05-01  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT SHF4960 Resin
VALOX™ PBT SHF4960 Resin
30%玻璃纤维增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release.
 
增强填料:含30%玻纤增强
含添加剂:脱模
材料特点:超高流动,阻燃V0,热稳定,高CTI
定属记号:PBT
塑料牌号:PBT SHF4960
加工方法:注射成型
销售电话:185 5121 3137 谭经理
销售地址:http://www.kingoflotto.com/sujiao/pbt/valox/shf4960-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 1270 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 1270 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2 % ASTM D 638
Tensile Modulus,5 mm/min 112100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1800 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 96300 kgf/cm² ASTM D 790
Tensile Stress,yield,5 mm/min 120 MPa ISO 527
Tensile Stress,break,5 mm/min 120 MPa ISO 527
Tensile Strain,yield,5 mm/min 2 % ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 11000 MPa ISO 527
Flexural Stress,yield,2 mm/min 185 MPa ISO 178
Flexural Stress,break,2 mm/min 185 MPa ISO 178
Flexural Strain,break,2 mm/min 2 % ISO 178
Flexural Modulus,2 mm/min 9600 MPa ISO 178
Hardness,H358/30 220 MPa ISO 2039-1
Hardness,Rockwell R 115 - ISO 2039-2
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ 45 kJ/m² ISO 179/2C
Charpy Impact,unnotched,-30℃ 40 kJ/m² ISO 179/2C
Izod Impact,unnotched,23℃ 60 cm-kgf/cm ASTM D 4812
Izod Impact,unnotched,-30℃ 59 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Izod Impact,notched,0℃ 8 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 611 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 40 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 40 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 9 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 0℃ 9 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 9 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 7 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 10 kJ/m² ISO 179/2C
Charpy Impact,notched,-30℃ 10 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 218 ASTM D 1525
Vicat Softening Temp,Rate B/50 205 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 220 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 210 ASTM D 648
CTE,-40℃ to 40℃,flow 2.4E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.3E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 2.5E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.6E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 218 ISO 306
Vicat Softening Temp,Rate B/50 205 ISO 306
Vicat Softening Temp,Rate B/120 200 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 220 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 210 ISO 75/Af
Relative Temp Index,Elec 130 UL 746B
Relative Temp Index,Mech w/impact 130 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.69 - ASTM D 792
Filler Content 30 % ASTM D 229
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.1-0.3 % SABIC Method
Mold Shrinkage,flow,3.2 mm(5) 0.1-0.3 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.4-0.7 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 9 g/10 min ASTM D 1238
Density 1.69 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.25 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Flow Rate,250℃/2.16 kg 8 g/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/2.16 kg 6 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/5.0 kg 50 cm³/10 min ISO 1133
Melt Viscosity,250℃,1500 sec-1 110 Pa-s ISO 11443
Melt Viscosity,260℃,1500 sec-1 68 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+11 Ohm-cm ASTM D 257
Hot Wire Ignition{PLC) 3 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 2 PLC Code UL 746A
Volume Resistivity 1.E+11 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+12 Ohm IEC 60093
Dielectric Strength,in oil,0.8 mm 35 kV/mm IEC 60243-1
Dielectric Strength in oil,1.5mm 24.5 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 24.5 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 17.8 kV/mm IEC 60243-1
Dissipation Factor,1 MHz 0.017 - IEC 60250
Comparative Tracking Index 275 V IEC 60112
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 0.8 mm UL 94
Glow Wire Flammability Index 960℃,passes at 0.75-1.5 mm IEC 60695-2-12
Glow Wire Ignitability Temperature,0.8 mm 700 IEC 60695-2-13
Glow Wire Ignitability Temperature,1.5 mm 700 IEC 60695-2-13
Oxygen Index(LOI) 32 % ISO 4589
Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-270
Nozzle Temperature 240-260
Front-Zone 3 Temperature 245-265
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-245
Hopper Temperature 40-60
Mold Temperature 40-100
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.