PBT HX3061HP Resin 挤出复合用

添加时间:2014-06-22  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT HX3061HP Resin
VALOX™ PBT HX3061HP Resin
非增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
 
产品说明
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity: 250C at 21.6 kgf is 1450-1850 poise. Available in Natural color (1001) only.
 
材料特点:熔体粘度:250℃/21.6公斤
材料用途:仅适用于复合/纤维
定属记号:PBT
塑料牌号:PBT HX3061HP
加工方法:挤出复合
销售电话:185 5121 3137 谭经理
销售地址:http://www.kingoflotto.com/sujiao/pbt/valox/hx3061hp.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50 mm/min 590 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50 mm/min 260 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50 mm/min 3.7 % ASTM D 638
Tensile Strain,brk,Type I,50 mm/min 140 % ASTM D 638
Tensile Modulus,5 mm/min 26500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 840 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 24400 kgf/cm² ASTM D 790
Tensile Stress,yield,50 mm/min 50 MPa ISO 527
Tensile Stress,break,50 mm/min 49 MPa ISO 527
Tensile Strain,yield,50 mm/min 3.2 % ISO 527
Tensile Strain,break,50 mm/min 8.6 % ISO 527
Tensile Modulus,1 mm/min 2600 MPa ISO 527
Flexural Stress,yield,2 mm/min 80 MPa ISO 178
Flexural Modulus,2 mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 3 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 254 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 3 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 167 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 120 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 49 ASTM D 648
CTE,-40℃ to 40℃,flow 7.6E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.8E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 7.6E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.8E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 173 ISO 306
Vicat Softening Temp,Rate B/120 169 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 49 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.31 - ASTM D 792
Mold Shrinkage,flow,3.2 mm (5) 1.5-2 % SABIC Method
Mold Shrinkage,xflow,3.2 mm (5) 1.5-2 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 50 g/10 min ASTM D 1238
Melt Viscosity 1650 poise SABIC Method
Density 1.31 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.34 % ISO 62
Moisture Absorption (23℃ / 50% RH) 0.08 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 45 cm³/10 min ISO 1133
Compounding Extrusion Value Unit
Drying Temperature 110-120
Drying Time 4-6 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0 %
Melt Temperature 245-260
Barrel-Zone 1 Temperature 200-230
Barrel-Zone 2 Temperature 240-255
Barrel-Zone 3 Temperature 240-275
Barrel-Zone 4 Temperature 240-275
Adapter Temperature 240-275
Die Temperature 240-275
Waterbath Temperature 25-35
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.