PBT DR51 Resin 含15%玻璃纤维增强

添加时间:2014-03-31  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT DR51 Resin
VALOX™ PBT DR51 Resin
15%玻璃纤维
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
VALOX DR51 is a 15% glass fiber reinforced PBT injection moulding resin with excellent mechanical, thermal and electrical performance. Applications: spotlights, appliance housings, handles.
 
增强填料:含15%玻璃纤维增强
材料特点:优良的机械性能,热性能和电气性能
材料用途:射灯,家电外壳,手柄
定属记号:PBT
塑料牌号:PBT DR51
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/dr51-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 910 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 910 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 3 % ASTM D 638
Tensile Modulus,5 mm/min 60100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1420 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 1420 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 45800 kgf/cm² ASTM D 790
Hardness,Rockwell R 118 - ASTM D 785
Taber Abrasion,CS-17,1 kg 16 mg/1000cy SABIC Method
Tensile Stress,yield,5 mm/min 95 MPa ISO 527
Tensile Stress,break,5 mm/min 100 MPa ISO 527
Tensile Strain,yield,5 mm/min 3 % ISO 527
Tensile Strain,break,5 mm/min 3 % ISO 527
Tensile Modulus,1 mm/min 6000 MPa ISO 527
Flexural Stress,yield,2 mm/min 150 MPa ISO 178
Flexural Stress,break,2 mm/min 155 MPa ISO 178
Flexural Strain,break,2 mm/min 5 % ISO 178
Flexural Modulus,2 mm/min 5100 MPa ISO 178
Hardness,H358/30 100 MPa ISO 2039-1
Hardness,Rockwell R 120 - ISO 2039-2
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ 30 kJ/m² ISO 179/2C
Charpy Impact,unnotched,-30℃ 27 kJ/m² ISO 179/2C
Izod Impact,unnotched,23℃ 33 cm-kgf/cm ASTM D 4812
Izod Impact,unnotched,-30℃ 33 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,notched,0℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 30 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 30 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 0℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -20℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -40℃ 4 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 4 kJ/m² ISO 179/2C
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
Charpy Impact,notched,-30℃ 4 kJ/m² ISO 179/2C
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 30 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 30 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 220 ASTM D 1525
Vicat Softening Temp,Rate B/50 210 ASTM D 1525
HDT,1.82 MPa,3.2mm,annealed 193 ASTM D 648
HDT,0.45 MPa,6.4 mm,unannealed 210 ASTM D 648
HDT,1.82 MPa,6.4 mm,unannealed 190 ASTM D 648
CTE,-40℃ to 40℃,flow 2.16E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.58E-05 1/℃ ASTM E 831
CTE,60℃ to 138℃,flow 2.16E-05 1/℃ ASTM E 831
Thermal Conductivity 0.19 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 3.35E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.06E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,flow 3.5E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 9.5E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,flow 3.4E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,xflow 1.83E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 220 ISO 306
Vicat Softening Temp,Rate B/50 210 ISO 306
Vicat Softening Temp,Rate B/120 205 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 210 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 175 ISO 75/Ae
Relative Temp Index,Elec 130 UL 746B
Relative Temp Index,Mech w/impact 130 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.45 - ASTM D 792
Specific Volume 0.71 cm³/g ASTM D 792
Filler Content 17 % ASTM D 229
Water Absorption,24 hours 0.07 % ASTM D 570
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.5-0.8 % SABIC Method
Mold Shrinkage,flow,1.5-3.2 mm(5) 0.4-0.6 % SABIC Method
Mold Shrinkage,flow,3.2-4.6 mm(5) 0.6-0.9 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.6-0.9 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2 mm(5) 0.5-0.8 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6 mm(5) 0.8-1.1 % SABIC Method
Melt Flow Rate,265℃/5.0 kgf 80 g/10 min ASTM D 1238
Density 1.45 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.2 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Flow Rate,250℃/2.16 kg 18 g/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/2.16 kg 15 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/5.0 kg 43 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/5.0 kg 65 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 170 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength,in air,3.2 mm 19.6 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6 mm 23.2 kV/mm ASTM D 149
Relative Permittivity,100 Hz 3.6 - ASTM D 150
Relative Permittivity,1 MHz 3.4 - ASTM D 150
Dissipation Factor,100 Hz 0.002 - ASTM D 150
Dissipation Factor,1 MHz 0.02 - ASTM D 150
Arc Resistance,Tungsten{PLC} 5 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 3 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 1 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 1 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 2 PLC Code UL 746A
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8 mm 26 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 24 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 18 kV/mm IEC 60243-1
Relative Permittivity,1 MHz 2.9 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,1 MHz 0.015 - IEC 60250
Comparative Tracking Index 300 V IEC 60112
Relative Permittivity,50/60 Hz 3 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 0.75 mm UL 94
UL Recognized,94HB Flame Class Rating 2nd value(3) 6 mm UL 94
Glow Wire Flammability Index 750℃,passes at 1 mm IEC 60695-2-12
Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-270
Nozzle Temperature 240-260
Front-Zone 3 Temperature 245-265
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-245
Hopper Temperature 40-60
Mold Temperature 40-100
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.