PBT 865 Resin 含30%玻纤增强,阻燃级

添加时间:2014-03-26  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT 865 Resin
VALOX™ PBT 865 Resin
30%玻纤增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and lighting parts.
 
增强填料:含30%玻纤增强
材料特点:PBT+PET共混物,表面光洁度佳,阻燃级
材料用途:外部外壳,蒸汽电熨斗,家电外壳和照明部件
定属记号:PBT
塑料牌号:PBT 865
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/865-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 1370 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 1370 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2 % ASTM D 638
Tensile Modulus,5 mm/min 112100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1880 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 1880 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 91700 kgf/cm² ASTM D 790
Tensile Stress,yield,5 mm/min 130 MPa ISO 527
Tensile Stress,break,5 mm/min 130 MPa ISO 527
Tensile Strain,yield,5 mm/min 2 % ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 11000 MPa ISO 527
Flexural Stress,yield,2 mm/min 195 MPa ISO 178
Flexural Stress,break,2 mm/min 195 MPa ISO 178
Flexural Strain,break,2 mm/min 3 % ISO 178
Flexural Modulus,2 mm/min 9200 MPa ISO 178
Hardness,H358/30 115 MPa ISO 2039-1
Hardness,Rockwell R 120 - ISO 2039-2
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ 55 kJ/m² ISO 179/2C
Charpy Impact,unnotched,-30℃ 50 kJ/m² ISO 179/2C
Izod Impact,unnotched,23℃ 74 cm-kgf/cm ASTM D 4812
Izod Impact,unnotched,-30℃ 73 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 7 cm-kgf/cm ASTM D 256
Izod Impact,notched,0℃ 7 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 7 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 50 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 0℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 7 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 8 kJ/m² ISO 179/2C
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy Impact,notched,-30℃ 8 kJ/m² ISO 179/2C
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 220 ASTM D 1525
Vicat Softening Temp,Rate B/50 200 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 215 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 195 ASTM D 648
CTE,-40℃ to 40℃,flow 1.96E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 6.05E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,flow 3.5E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 1.E-04 1/℃ ISO 11359-2
CTE,23℃ to 150℃,flow 1.68E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,xflow 1.48E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 220 ISO 306
Vicat Softening Temp,Rate B/50 200 ISO 306
Vicat Softening Temp,Rate B/120 200 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 215 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 195 ISO 75/Ae
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 215 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 195 ISO 75/Af
Relative Temp Index,Elec 110 UL 746B
Relative Temp Index,Mech w/impact 110 UL 746B
Relative Temp Index,Mech w/o impact 110 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.65 - ASTM D 792
Filler Content 30 % ASTM D 229
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.4-0.8 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.6-1 % SABIC Method
Melt Flow Rate,266℃/5.0 kgf 70 g/10 min ASTM D 1238
Density 1.65 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.32 % ISO 62
Moisture Absorption(23℃/50% RH) 0.03 % ISO 62
Melt Volume Rate,MVR at 250℃/5.0 kg 23 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/1.2 kg 7 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/2.16 kg 15 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/5.0 kg 50 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 145 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+15 Ohm-cm ASTM D 257
Dielectric Strength,in oil,0.8 mm 25 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6 mm 19 kV/mm ASTM D 149
Dielectric Strength,in oil,3.2 mm 15 kV/mm ASTM D 149
Arc Resistance,Tungsten{PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 1 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 4 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 3 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 3 PLC Code UL 746A
Volume Resistivity 1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8 mm 25 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 19 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 15 kV/mm IEC 60243-1
Relative Permittivity,1 MHz 3.3 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,1 MHz 0.012 - IEC 60250
Comparative Tracking Index 225 V IEC 60112
Comparative Tracking Index,M 150 V IEC 60112
Relative Permittivity,50/60 Hz 3.4 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 1.5 mm UL 94
UL Recognized,94-5VA Rating(3) 3 mm UL 94
Glow Wire Flammability Index 960℃,passes at 1 mm IEC 60695-2-12
Oxygen Index(LOI) 31 % ISO 4589
Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 4-6 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260-285
Nozzle Temperature 265-275
Front-Zone 3 Temperature 260-280
Middle-Zone 2 Temperature 255-280
Rear-Zone 1 Temperature 240-260
Hopper Temperature 40-60
Mold Temperature 60-110
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.