PBT 7062HP Resin 含38%矿物填充

添加时间:2014-03-25  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT 7062HP Resin
VALOX™ PBT 7062HP Resin
38%矿物填充
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
ENDURAN 7062HP is a 38% mineral filled & FDA compliance injection moulding resin.
 
增强填料:含38%矿物填充
材料特点:符合FDA
定属记号:PBT
塑料牌号:PBT 7062HP
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/7062hp-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 540 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 560 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 3 % ASTM D 638
Tensile Modulus,5 mm/min 42000 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3 mm/min,50 mm span 1120 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 45600 kgf/cm² ASTM D 790
Taber Abrasion,CS-17,1 kg 74 mg/1000cy SABIC Method
Tensile Stress,yield,5 mm/min 60 MPa ISO 527
Tensile Stress,break,5 mm/min 60 MPa ISO 527
Tensile Strain,yield,5 mm/min 3 % ISO 527
Tensile Strain,break,5 mm/min 3 % ISO 527
Tensile Modulus,1 mm/min 4200 MPa ISO 527
Flexural Stress,break,2 mm/min 100 MPa ISO 178
Flexural Modulus,2 mm/min 3900 MPa ISO 178
Hardness,H358/30 140 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 43 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 2 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 2 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 50 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 30 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 30 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 3 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 3 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 2 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 2 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 37 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 33 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 175 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 69 ASTM D 648
CTE,-40℃ to 40℃,flow 9.E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.E-05 1/℃ ASTM E 831
Thermal Conductivity 0.32 W/m-℃ ISO 8302
CTE,23℃ to 80℃,flow 9.E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 9.E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,flow 1.1E-04 1/℃ ISO 11359-2
CTE,23℃ to 150℃,xflow 1.1E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 215 ISO 306
Vicat Softening Temp,Rate B/50 175 ISO 306
Vicat Softening Temp,Rate B/120 175 ISO 306
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 65 ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.81 - ASTM D 792
Mold Shrinkage,flow,3.2 mm(5) 1.2-1.9 % SABIC Method
Melt Flow Rate,266℃/1.2 kgf 33 g/10 min ASTM D 1238
Density 1.81 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.07 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Volume Rate,MVR at 265℃/1.2 kg 21 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/2.16 kg 41 cm³/10 min ISO 1133
Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255-280
Nozzle Temperature 245-270
Front-Zone 3 Temperature 250-270
Middle-Zone 2 Temperature 240-260
Rear-Zone 1 Temperature 230-250
Hopper Temperature 40-60
Mold Temperature 60-100
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.