VALOX PBT 420SE0U Resin
VALOX™ PBT 420SE0U Resin
30%玻璃纤维增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
 
产品说明
PBT, 30% Glass Reinforced, Flame Retardant UL94 V-0/5VA rated, UV-Stabilized
 
增强填料:含30%玻纤增强
材料特点:阻燃UL94 V-0/5VA,抗紫外线稳定
定属记号:PBT
塑料牌号:PBT 420SE0U
销售电话:185 5121 3137 谭经理
销售地址:http://www.kingoflotto.com/sujiao/pbt/valox/420se0u.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 1220 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 1220 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2 % ASTM D 638
Tensile Modulus,5 mm/min 122300 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3 mm/min,50 mm span 1890 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 99900 kgf/cm² ASTM D 790
Hardness,Rockwell R 119 - ASTM D 785
Tensile Stress,yield,5 mm/min 120 MPa ISO 527
Tensile Stress,break,5 mm/min 120 MPa ISO 527
Tensile Strain,yield,5 mm/min 1.9 % ISO 527
Tensile Strain,break,5 mm/min 1.9 % ISO 527
Tensile Modulus,1 mm/min 10000 MPa ISO 527
Flexural Stress 180 MPa ISO 178
Flexural Modulus,2 mm/min 9500 MPa ISO 178
Hardness,H358/30 118 MPa ISO 2039-1
Hardness,Rockwell R 119 - ISO 2039-2
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 63 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 6 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 50 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 45 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 6 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 7 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 6 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 200 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 212 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 200 ASTM D 648
HDT,0.45 MPa,6.4 mm,unannealed 215 ASTM D 648
HDT,1.82 MPa,6.4 mm,unannealed 204 ASTM D 648
CTE,-40℃ to 40℃,flow 2.5E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.9E-05 1/℃ ASTM E 831
CTE,60℃ to 138℃,flow 2.52E-05 1/℃ ASTM E 831
Thermal Conductivity 0.25 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 2.5E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.9E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 220 ISO 306
Vicat Softening Temp,Rate B/50 200 ISO 306
Vicat Softening Temp,Rate B/120 200 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 220 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 200 ISO 75/Af
Relative Temp Index,Elec 130 UL 746B
Relative Temp Index,Mech w/impact 130 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.63 - ASTM D 792
Specific Volume 0.61 cm³/g ASTM D 792
Water Absorption,24 hours 0.06 % ASTM D 570
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.1-0.5 % SABIC Method
Mold Shrinkage,flow,3.2 mm(5) 0.5-0.7 % SABIC Method
Mold Shrinkage,flow,1.5-3.2 mm(5) 0.3-0.5 % SABIC Method
Mold Shrinkage,flow,3.2-4.6 mm(5) 0.5-0.8 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.4-0.8 % SABIC Method
Mold Shrinkage,xflow,3.2 mm(5) 0.5-1 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2 mm(5) 0.4-0.6 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6 mm(5) 0.6-0.9 % SABIC Method
Melt Flow Rate,250℃/5.0 kgf 42 g/10 min ASTM D 1238
Density 1.63 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.09 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Volume Rate,MVR at 250℃/5.0 kg 29 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength,in air,3.2 mm 19 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6 mm 24 kV/mm ASTM D 149
Relative Permittivity,100 Hz 3.8 - ASTM D 150
Relative Permittivity,1 MHz 3.7 - ASTM D 150
Dissipation Factor,100 Hz 0.002 - ASTM D 150
Dissipation Factor,1 MHz 0.02 - ASTM D 150
Arc Resistance,Tungsten{PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 4 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 3 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-2 Flame Class Rating(3) 0.4 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 0.71 mm UL 94
UL Recognized,94-5VA Rating(3) 2 mm UL 94
Oxygen Index(LOI) 32 % ASTM D 2863
UV-light,water exposure/immersion F2 - UL 746C
Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255-275
Nozzle Temperature 250-270
Front-Zone 3 Temperature 255-275
Middle-Zone 2 Temperature 250-270
Rear-Zone 1 Temperature 245-265
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.