VALOX PBT 420HP Resin
VALOX™ PBT 420HP Resin
30%玻璃填充
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
30% Glass filled PBT resin, FDA Food Contact compliant in limited colors.
 
增强填料:含30%玻璃填充
材料特点:符合FDA食品接触
定属记号:PBT
塑料牌号:PBT 420HP
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/420hp-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 1220 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 1220 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 3 % ASTM D 638
Tensile Modulus,5 mm/min 94800 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3 mm/min,50 mm span 1920 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 77300 kgf/cm² ASTM D 790
Hardness,Rockwell R 118 - ASTM D 785
Tensile Stress,yield,5 mm/min 125 MPa ISO 527
Tensile Stress,break,5 mm/min 125 MPa ISO 527
Tensile Strain,yield,5 mm/min 2 % ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 9300 MPa ISO 527
Flexural Stress,yield,2 mm/min 195 MPa ISO 178
Flexural Modulus,2 mm/min 8500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 81 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 81 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 45 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 7 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 45 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 45 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 215 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 220 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 203 ASTM D 648
HDT,0.45 MPa,6.4 mm,unannealed 215 ASTM D 648
CTE,-40℃ to 40℃,flow 2.52E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 1.2E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 2.52E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 1.2E-04 1/℃ ISO 11359-2
Vicat Softening Temp,Rate A/50 223 ISO 306
Vicat Softening Temp,Rate B/50 215 ISO 306
Vicat Softening Temp,Rate B/120 215 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 217 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 204 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.53 - ASTM D 792
Specific Volume 0.65 cm³/g ASTM D 792
Filler Content 30 % ASTM D 229
Water Absorption,24 hours 0.06 % ASTM D 570
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.3-0.7 % SABIC Method
Mold Shrinkage,flow,3.2 mm(5) 0.3-0.8 % SABIC Method
Mold Shrinkage,flow,1.5-3.2 mm(5) 0.3-0.5 % SABIC Method
Mold Shrinkage,flow,3.2-4.6 mm(5) 0.5-0.8 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.5-1 % SABIC Method
Mold Shrinkage,xflow,3.2 mm(5) 0.5-1 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2 mm(5) 0.4-0.6 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6 mm(5) 0.6-0.9 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 17 g/10 min ASTM D 1238
Density 1.53 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.26 % ISO 62
Moisture Absorption(23℃/50% RH) 0.08 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 13 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >3.2E+16 Ohm-cm ASTM D 257
Dielectric Strength,in air,3.2 mm 18.7 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6 mm 24.8 kV/mm ASTM D 149
Relative Permittivity,100 Hz 3.8 - ASTM D 150
Relative Permittivity,1 MHz 3.7 - ASTM D 150
Dissipation Factor,100 Hz 0.002 - ASTM D 150
Dissipation Factor,1 MHz 0.02 - ASTM D 150
Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.