PBT 4012 Resin 含10%玻璃纤维增强

添加时间:2014-03-20  信息来源:http://www.kingoflotto.com/  作者:苏州希普能塑料
VALOX PBT 4012 Resin
VALOX™ PBT 4012 Resin
10%玻璃纤维
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors.
 
增强填料:含10%玻璃纤维增强
材料特点:高强度
材料用途:连接器
定属记号:PBT
塑料牌号:PBT 4012
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/4012-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 830 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 830 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 3 % ASTM D 638
Tensile Modulus,5 mm/min 47900 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1320 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 41800 kgf/cm² ASTM D 790
Tensile Stress,yield,5 mm/min 85 MPa ISO 527
Tensile Stress,break,5 mm/min 85 MPa ISO 527
Tensile Strain,yield,5 mm/min 3.2 % ISO 527
Tensile Strain,break,5 mm/min 3.5 % ISO 527
Tensile Modulus,1 mm/min 4500 MPa ISO 527
Flexural Stress,break,2 mm/min 115 MPa ISO 178
Flexural Strain,break,2 mm/min 6 % ISO 178
Flexural Modulus,2 mm/min 3900 MPa ISO 178
Hardness,H358/30 117 MPa ISO 2039-1
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ 35 kJ/m² ISO 179/2C
Charpy Impact,unnotched,-30℃ 35 kJ/m² ISO 179/2C
Izod Impact,notched,23℃ 7 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 7 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 30 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 28 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 28 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 5 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 5 kJ/m² ISO 179/2C
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
Charpy Impact,notched,-30℃ 5 kJ/m² ISO 179/2C
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 40 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 40 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 224 ASTM D 1525
Vicat Softening Temp,Rate B/50 206 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 150 ASTM D 648
CTE,-40℃ to 40℃,flow 6.E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.E-05 1/℃ ASTM E 831
CTE,23℃ to 80℃,flow 6.E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 8.E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,xflow 8.5E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 224 ISO 306
Vicat Softening Temp,Rate B/50 206 ISO 306
Vicat Softening Temp,Rate B/120 204 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 215 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 170 ISO 75/Ae
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 210 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 150 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.36 - ASTM D 792
Filler Content 6 % ASTM D 229
Mold Shrinkage on Tensile Bar,flow(2)(5) 0.5-0.7 % SABIC Method
Mold Shrinkage,flow,3.2 mm(5) 0.6-1.6 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.7-1 % SABIC Method
Melt Flow Rate,250℃/1.2 kgf 13 g/10 min ASTM D 1238
Density 1.36 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.2 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Volume Rate,MVR at 250℃/1.2 kg 11 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/2.16 kg 18 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/5.0 kg 46 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 110 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8 mm 30 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 25 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity,1 MHz 3 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,1 MHz 0.014 - IEC 60250
Comparative Tracking Index 250 V IEC 60112
Comparative Tracking Index,M 150 V IEC 60112
Relative Permittivity,50/60 Hz 3.1 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94HB Flame Class Rating(3)(4) 0.8 mm UL 94 by SABIC-IP
Glow Wire Flammability Index 750℃,passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature,1.0 mm 775 IEC 60695-2-13
Glow Wire Ignitability Temperature,1.5 mm 775 IEC 60695-2-13
Glow Wire Ignitability Temperature,2.0 mm 750 IEC 60695-2-13
Glow Wire Ignitability Temperature,3.0 mm 725 IEC 60695-2-13
Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-270
Nozzle Temperature 240-260
Front-Zone 3 Temperature 245-265
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-245
Hopper Temperature 40-60
Mold Temperature 40-100
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.