VALOX PBT 310SE0 Resin
VALOX™ PBT 310SE0 Resin
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
 
产品说明
VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.
 
材料特点:未增强,阻燃PBT
材料用途:电器行业,线轴,电器外壳,键盘,开关和开关元件
定属记号:PBT
塑料牌号:PBT 310SE0
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.kingoflotto.com/sujiao/pbt/valox/310se0-resin.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50 mm/min 610 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50 mm/min 400 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50 mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,50 mm/min 15 % ASTM D 638
Tensile Modulus,5 mm/min 27500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1020 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 26700 kgf/cm² ASTM D 790
Taber Abrasion,CS-17,1 kg 19 mg/1000cy SABIC Method
Tensile Stress,yield,50 mm/min 60 MPa ISO 527
Tensile Stress,break,50 mm/min 40 MPa ISO 527
Tensile Strain,yield,50 mm/min 5 % ISO 527
Tensile Strain,break,50 mm/min 15 % ISO 527
Tensile Modulus,1 mm/min 2700 MPa ISO 527
Flexural Stress,yield,2 mm/min 90 MPa ISO 178
Flexural Modulus,2 mm/min 2500 MPa ISO 178
Hardness,H358/30 150 MPa ISO 2039-1
Hardness,Rockwell R 120 - ISO 2039-2
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ NB kJ/m² ISO 179/2C
Charpy Impact,unnotched,-30℃ NB kJ/m² ISO 179/2C
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,unnotched,-30℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,notched,0℃ 4 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 4 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 2039 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 0℃ 5 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 5 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 6 kJ/m² ISO 179/2C
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 4 kJ/m² ISO 179/1eA
Charpy Impact,notched,-30℃ 5 kJ/m² ISO 179/2C
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 212 ASTM D 1525
Vicat Softening Temp,Rate B/50 170 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 160 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 75 ASTM D 648
HDT,0.45 MPa,6.4 mm,unannealed 162 ASTM D 648
HDT,1.82 MPa,6.4 mm,unannealed 71 ASTM D 648
CTE,-40℃ to 40℃,flow 7.92E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.92E-05 1/℃ ASTM E 831
CTE,60℃ to 138℃,flow 1.31E-04 1/℃ ASTM E 831
Thermal Conductivity 0.24 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 7.6E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.3E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,flow 1.E-04 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 1.E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 212 ISO 306
Vicat Softening Temp,Rate B/50 170 ISO 306
Vicat Softening Temp,Rate B/120 170 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 160 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 60 ISO 75/Ae
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 75 ISO 75/Af
Relative Temp Index,Elec 120 UL 746B
Relative Temp Index,Mech w/impact 120 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.4 - ASTM D 792
Specific Volume 0.71 cm³/g ASTM D 792
Mold Shrinkage on Tensile Bar,flow(2)(5) 1.1-1.8 % SABIC Method
Mold Shrinkage,flow,3.2 mm(5) 1.5-2.3 % SABIC Method
Mold Shrinkage,flow,0.75-2.3 mm(5) 0.9-1.6 % SABIC Method
Mold Shrinkage,flow,2.3-4.6 mm(5) 1.5-2.3 % SABIC Method
Mold Shrinkage on Tensile Bar,xflow(2)(5) 0.9-1.9 % SABIC Method
Mold Shrinkage,xflow,0.75-2.3 mm(5) 1-1.7 % SABIC Method
Mold Shrinkage,xflow,2.3-4.6 mm(5) 1.6-2.4 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 8.6 g/10 min ASTM D 1238
Melt Flow Rate,265℃/5.0 kgf 33 g/10 min ASTM D 1238
Melt Flow Rate,266℃/5.0 kgf 33 g/10 min ASTM D 1238
Density 1.4 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.36 % ISO 62
Moisture Absorption(23℃/50% RH) 0.08 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 8 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 250℃/5.0 kg 15 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/5.0 kg 30 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 260 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength,in air,3.2 mm 18.4 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6 mm 26 kV/mm ASTM D 149
Dielectric Strength,in oil,3.2 mm 18 kV/mm ASTM D 149
Relative Permittivity,1 MHz 3 - ASTM D 150
Dissipation Factor,1 MHz 0.015 - ASTM D 150
Arc Resistance,Tungsten{PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 4 PLC Code UL 746A
High Voltage Arc Resistance{PLC) 6 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 3 PLC Code UL 746A
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,shorttime,1.0mm 18 kV/mm IEC 60243-1
Dielectric Strength,in oil,0.8 mm 39 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 26 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 18 kV/mm IEC 60243-1
Relative Permittivity,100 Hz 3.1 - IEC 60250
Relative Permittivity,1 MHz 3 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,100 Hz 0.002 - IEC 60250
Dissipation Factor,1 MHz 0.015 - IEC 60250
Comparative Tracking Index 175 V IEC 60112
Comparative Tracking Index,M 100 V IEC 60112
Relative Permittivity,50/60 Hz 2.9 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 0.71 mm UL 94
UL Recognized,94-5VA Rating(3) 3 mm UL 94
Glow Wire Flammability Index 960℃,passes at 1 mm IEC 60695-2-12
Oxygen Index(LOI) 30 % ISO 4589
Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 245-260
Nozzle Temperature 240-255
Front-Zone 3 Temperature 245-260
Middle-Zone 2 Temperature 240-255
Rear-Zone 1 Temperature 230-250
Mold Temperature 50-75
Back Pressure 0.3-0.7 MPa
Screw Speed 50-100 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.013-0.025 mm
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.